The M-ABS is available in 12 colours. Samples of 50gr. are available (in black only). Make your choice! By selecting a variation, only the products available for that variation will appear in the other 2 variations. Example: by choosing the weight variation 50gr., only the colors and extrusion diameter available for this variation will appear.
M-ABS is a transparent ABS filament, extremely strong, durable (in the service life) and shock resistant. Due to the low percentage of butadiene in M-ABS, this filament has a much less unpleasant smell than ABS and, moreover, also has less retraction. M-ABS polymer is inherently less impact resistant than ABS, but this slightly modified M-ABS filament is approx. 3 times more impact resistant than any other conventional PLA on the market. The transparency of the polymer also makes it possible to manufacture deep opaque colors, if desired.
Directions for use:
– The recommended temperature for the heating mat is ± 90 – 110°C. We recommend using a hook like the EZ Stick (for any type of parts), an adhesive such as Kapton (for small parts), glue (for large parts), or even both (Kapton and glue). If you use glue, no need to put it on the entire surface of the part, but only on the contours or areas at risk of retraction.
– M-ABS can be used on all filament deposition 3D printers.
– Our filaments are filmed, in a cardboard box without window filmed also to ensure the good conservation of the product until the moment of use.
– Store it in a cold and dry environment (15 – 25 ° C), away from light (UV) and under vacuum (to stay dry). We recommend that, after each use, you vacuum it by slipping a silica gel pouch into it and in its box protected from UV. Good storage significantly increases the shelf life of your filament.
Size Ø Round tolerance
1.75mm. ± 0.05mm. ≥ 95%
Specific density: ASTM D792 – 1.06gr./cc.
MFR 220°C/10kg. : ISO 1133 – 11gr/10min.
Tensile strength: ISO 527 – 39mpa.
Elongation at break: ISO 527 – 45%
Traction module: ISO 527 – 1780mpa.
Bending module: ISO 178 – 1800mpa.
Flexural strength: ISO 178 – 59mpa.
Impact resistance Izod method 23°C: ISO 180/A – 22kj./m².
Transparency: ISO 13468 – 90%
Temp. Printing: DF – 245 ± 10°C
Temp. Fusion: ISO 294 – 225 ± 15°C
Temp. Flexing: ISO 75 – 69°C
Click on this link to get the data sheet:
Click on this link to get the safety data sheet: