PLA filaments 1.75 and 2.85 mm. https://mcpp-3dp.com/pla/
Polylactic Acid (PLA) is a biodegradable plastic (made from renewable natural resources), making it very popular for 3D printing. PLA is a high-quality thermoplastic that is robust and easy to print. It has been slightly modified making it more resistant and less brittle than other PLA on the market, while retaining its typical PLA characteristics. Due to a low retraction factor, the PLA will not deform after cooling.
Pla is available in 28 colors. Filaments of 2.85mm. in 1kg. are available (limited color). Coils of 2.3kg., 4.5kg. and 8.5kg. are available (limited color). Samples of 50gr. are available. Make your choice! By selecting a variation, only the products available for that variation will appear in the other 2 variations. Example: by choosing the 2.3kg weight variation, only the colors and extrusion diameter available for this variation will appear.
Directions for use:
– The recommended temperature for the heating mat is ± 35 – 60°C. Due to its low tendency to retract, PLA can also be printed without a heating mat. Despite its low tendency to retract, we recommend using a hook like The EZ Stick (for all types of parts), an adhesive such as Blue Tape or PET (for small parts), glue (for large parts), or even both (Blue Tape or PET and glue). If you use glue, no need to put it on the entire surface of the part, but only on the contours or areas at risk of retraction.
– PLA can be used on all filament deposition 3D printers.
– Our filaments are filmed, in a cardboard box without window filmed also to ensure the good conservation of the product until the moment of use.
– Store it in a cold and dry environment (15 – 25 ° C), away from light (UV) and under vacuum (to stay dry). We recommend that, after each use, you vacuum it by slipping a silica gel pouch into it and in its box protected from UV. Good storage significantly increases the shelf life of your filament.
Size Ø Round tolerance
1.75mm. ± 0.05mm. ≥ 95%
Specific density: ISO 1183 – 1.24gr./cc.
MFR 210°C/2.16kg. : ISO 1183 – 9.56gr./10min.
Tensile strength: ISO 527 – 70mpa.
Elongation at efficiency: ISO 527 – 5%
Elongation at break: ISO 527 – 20%
Traction module: ISO 527 – 3120mpa.
Impact resistance Charpy method 23°C: ISO 179 – 3.4kj./m².
Moisture absorption: ISO 62 – 1968ppm.
Temp. Printing: DF – 205 ± 10°C
Temp. Melting: ISO 11357 – 115 ± 35°C
Temp. Vicat softening: ISO 306 – 60°C
Temp. glass transition: ISO 11357 – 57°C
In the event of a breakup, we offer Swiss quality PLA